钴基复合氧化物氧化降解甲苯的结构与催化性能

doi:10.3969/j.cnki.jdxb.2018.03.013

摘要/Abstract

摘要：

采用溶胶-凝胶法制备了钴基复合氧化物A-Co（A=Cu,Mn,Ce）,测定和评价了A-Co复合催化剂氧化降解甲苯的催化性能.结果表明,二元钴基复合氧化物氧化降解甲苯的催化活性均优于纯钴氧化物催化剂,其中,Ce-Co氧化物的t10和t90(分别为达到10%和90%的甲苯转化的温度)分别为221,238 ℃,催化活性最高.在240 ℃连续使用50 h,Ce-Co氧化降解甲苯降解转化率仍为99%以上,具有较好的催化稳定性.应用X射线衍射、氮气吸脱附、扫描电子显微镜、氢气程序升温还原和X射线光电子能谱等表征技术，研究了钴基催化剂的结构与催化性能的关系,在Ce-Co催化剂上形成的Ce⁴⁺/Ce³⁺和Co³⁺/Co²⁺氧化还原对促进了催化剂上氧的迁移,提高了表面氧的可还原性,在甲苯氧化降解过程中产生协同作用.

关键词： 催化氧化, 钴基氧化物, 溶胶-凝胶, VOC, 甲苯

Abstract:

Cobalt-based oxides A-Co (A=Cu,Mn,Ce) and pure cobalt oxide prepared by using sol-gel method have been tested for toluene oxidation.It is found that all binary cobalt-based oxides showed higher catalytic performance in the oxidation of toluene than pure cobalt oxide.The most efficient catalyst was Ce-Co with t10 and t90 (the temperature required for achieving 10% and 90% conversion of toluene,respectively) values of 221 and 238 ℃,respectively.In addition,the stability of the Ce-Co oxide was evaluated at 99% of toluene conversion at 240 ℃ for 50 hours.The characterization techniques of X-ray diffractometry,nitrogen adsorption-desorption,scanning electron microscope,H2 temperature programmed reduction and X-ray photoelectron spectroscopy were used to explain the improved catalytic performance.The results indicated that Ce⁴⁺/Ce³⁺ and Co³⁺/Co²⁺ redox couples in the Ce-Co catalyst facilitated the mobility of oxygen and improved the reducibility of surface oxygen accounting for the synergetic effect in the oxidation of toluene.

Key words: catalytic oxidation, Co-based oxides, sol-gel, VOC, toluene

胡秀珍,蒋崇文,朱俊东,龙杰,宋曲之. 钴基复合氧化物氧化降解甲苯的结构与催化性能[J]. 吉首大学学报（自然科学版）, DOI: 10.3969/j.cnki.jdxb.2018.03.013.

HU Xiuzhen,JIANG Chongwen,ZHU Jundong,LONG Jie,SONG Quzhi. Structure of the Cobalt-Based Oxide and Its Catalytic Performance in Oxidation of Toluene[J]. Journal of Jishou University（Natural Sciences Edition), DOI: 10.3969/j.cnki.jdxb.2018.03.013.

参考文献

[1] HUANG H B,XU Y,FENG Q Y,et al.Low Temperature Catalytic Oxidation of Volatile Organic Compounds:A Review[J].Catalysis Science & Technology,2015,5(5):2 649-2 669.
[2] TANG W X,WU X F,LI S D,et al.Co-Nanocasting Synthesis of Mesoporous Cu-Mn Composite Oxides and Their Promoted Catalytic Activities for Gaseous Benzene Removal[J].Applied Catalysis B:Environmental,2015,162:110-121.
[3] JI Y M,ZHAO J,TERAZONO H,et al.Reassessing the Atmospheric Oxidation Mechanism of Toluene[J].Proceedings of the National Academy of Sciences of the United States of America,2017,114(31):8 169-8 174.
[4] LEE-TAYLOR J,MADRONICH S,AUMONT B,et al.Explicit Modeling of Organic Chemistry and Secondary Organic Aerosol Partitioning for Mexico City and Its Outflow Plume[J].Atmospheric Chemistry and Physics,2011,11(24):13 219-13 241.
[5] ROKICINSKA A,DROZDEK M,DUDEK B,et al.Cobalt-Containing BEA Zeolite for Catalytic Combustion of Toluene[J].Applied Catalysis B:Environmental,2017,212:59-67.
[6] YI H H,YANG Z Y,TANG X L,et al.Promotion of Low Temperature Oxidation of Toluene Vapor Derived from the Combination of Microwave Radiation and Nano-Size Co3O4[J].Chemical Engineering Journal,2018,333:554-563.
[7] BEHAR S,GMEZ-MENDOZA N ,GOMEZ-GARCIA M A,et al.Study and Modelling of Kinetics of the Oxidation of VOC Catalyzed by Nanosized Cu-Mn Spinels Prepared via an Alginate Route[J].Applied Catalysis A:General,2015,504:203-210.
[8] SIHAIB Z,PULEO F,GARCIA-VARGAS J M,et al.Manganese Oxide-Based Catalysts for Toluene Oxidation[J].Applied Catalysis B:Environmental,2017,209:689-700.
[9] TANG W X,WU X F,LIU G,et al.Preparation of Hierarchical Layer-Stacking Mn-Ce Composite Oxide for Catalytic Total Oxidation of VOCs[J].Journal of Rare Earths,2015,33(1):62-69.
[10] ABOUKAIS A,SKAF MS,HANY S,et al.A Comparative Study of Cu,Ag and Au Doped CeO2 in the Total Oxidation of Volatile Organic Compounds (VOCs)[J].Materials Chemistry and Physics,2016,177:570-576.
[11] HE C,LI J R,ZHANG X Y,et al.Highly Active Pd-Based Catalysts with Hierarchical Pore Structure for Toluene Oxidation:Catalyst Property and Reaction Determining Factor[J].Chemical Engineering Journal,2012,180(1):46-56.
[12] SANZ O,DELGADO J J,NAVARRO P,et al.VOCs Combustion Catalyzed by Platinum Supported on Manganese Octahedral Molecular Sieves[J].Applied Catalysis B:Environmental,2011,110(45):231-237.
[13] SOLSONA B,AYLO'N E,MURILLO R,et al.Deep Oxidation of Pollutants Using Gold Deposited on a High Surface Area Cobalt Oxide Prepared by a Nanocasting Route[J].Journal of Hazardous Materials,2011,187(1/2/3):544-552.
[14] CAI T,HUANG H,DENG W,et al.Catalytic Combustion of 1,2-Dichlorobenzene at Low Temperature over Mn-Modified Co3O4 Catalysts[J].Applied Catalysis B:Environmental,2015,166/197:393-405.
[15] REN Q,MO S,PENG R,et al.Controllable Synthesis of 3D Hierarchical Co3O4 Nanocatalysts with Various Morphologies for the Catalytic Oxidation of Toluene[J].Journal of Materials Chemistry A,2018,6(2):498-509.
[16] CARABINEIRO S A C,CHEN X,KONSOLAKIS M,et al.Catalytic Oxidation of Toluene on Ce-Co and La-Co Mixed Oxides Synthesized by Exotemplating and Evaporation Methods[J].Catalysis Today,2015,244:161-171.
[17] GOMEZ D M,GALVITA V V,GATICA J M,et al.TAP Study of Toluene Total Oxidation over a Co3O4/La-CeO2 Catalyst with an Application as a Washcoat of Cordierite Honeycomb Monoliths[J].Physical Chemistry Chemical Physics,2014,16(23):11 447-11 455.
[18] GARCIA T,AGOURAM S,SANCHEZ-ROYO J F,et al.Deep Oxidation of Volatile Organic Compounds Using Ordered Cobalt Oxides Prepared by a Nanocasting Route[J].Applied Catalysis A:General,2010,386(1/2):16-27.
[19] HU F Y,CHEN J J,PENG Y,et al.Novel Nanowire Self-Assembled Hierarchical CeO2 Microspheres for Low Temperature Toluene Catalytic Combustion[J].Chemical Engineering Journal,2018,331:425-434.
[20] JIANG S J,SONG S Q.Enhancing the Performance of Co3O4/CNTs for the Catalytic Combustion of Toluene by Tuning the Surface Structures of CNTs[J].Applied Catalysis B:Environmental,2013,140:1-8.
[21] DU Y C,MENG Q,WANG J S,et al.Three-Dimensional Mesoporous Manganese Oxides and Cobalt Oxides:High-Efficiency Catalysts for the Removal of Toluene and Carbon Monoxide[J].Microporous and Mesoporous Materials,2012,162:199-206.
[22] HOSSEINI S A,NIAEI A,SALARI D,et al.Nanocrystalline AMn2O4 (A=Co,Ni,Cu) Spinels for Remediation of Volatile Organic Compounds—Synthesis,Characterization and Catalytic Performance[J].Ceramics International,2012,38(2):1 655-1 661.
[23] HOSSEINI S A,NIAEI A,SALARI D,et al.Study of Correlation Between Activity and Structural Properties of Cu-(Cr,Mn and Co)2 Nano Mixed Oxides in VOC Combustion[J].Ceramics International,2014,40(4):6 157-6 163.
[24] HOSSEINI S A,ALVAREZ-GALVAN M C,FIERRO J L G,et al.MCr2O4 (M=Co,Cu,and Zn) Nanospinels for 2-Propanol Combustion:Correlation of Structural Properties with Catalytic Performance and Stability[J].Ceramics International,2013,39(8):9 253-9 261.
[25] LIOTTA L F,WU F,PANTALEO G,et al.Co3O4 Nanocrystals and Co3O4-MOx Binary Oxides for CO,CH4 and VOC Oxidation at Low Temperatures:A Review[J].Catalysis Science & Technology,2013,3(12):3 085-3 102.
[26] LIAO Y N,ZHANG X,PENG R S,et al.Catalytic Properties of Manganese Oxide Polyhedra with Hollow and Solid Morphologies in Toluene Removal[J].Applied Surface Science,2017,405:20-28.
[27] LIOTTA L F,OUSMANE M,DI CARLO G,et al.Catalytic Removal of Toluene over Co3O4-CeO2 Mixed Oxide Catalysts:Comparison with Pt/Al2O3 [J].Catalysis Letters,2008,127(3/4):270-276.
[28] AGUILERA D A,PEREZ A,MOLINA R,et al.Cu-Mn and Co-Mn Catalysts Synthesized from Hydrotalcites and Their Use in the Oxidation of VOCs[J].Applied Catalysis B:Environmental,2011,104(1/2):144-150.
[29] SCHUBERT M M,HACKENBERG S,VAN VEEN A C,et al.CO Oxidation over Supported Gold Catalysts-"Inert" and "Active" Support Materials and Their Role for the Oxygen Supply During Reaction[J].Journal of Catalysis,2001,197(1):113-122.
[30] LIU Y Xi,DAI H X,DENG J G,et al.Mesoporous Co3O4-Supported Gold Nanocatalysts:Highly Active for the Oxidation of Carbon Monoxide,Benzene,Toluene,and o-Xylene[J].Journal of Catalysis,2014,309:408-418.
[31] WANG C,ZHANG C H,HUA W C,et al.Catalytic Oxidation of Vinyl Chloride Emissions over Co-Ce Composite Oxide Catalysts[J].Chemical Engineering Journal,2017,315:392-402.
[32] ZHANG X P,WANG J X,TAN B J,et al.Ce-Co Catalyst with High Surface Area and Uniform Mesoporous Channels Prepared by Template Method for H0g Oxidation[J].Catalysis Communications,2017,98:5-8.
[33] HOSSEINI S A,SALARI D,NIAEI A,et al.Chemical-Physical Properties of Spinel CoMn2O4 Nano-Powders and Catalytic Activity in the 2-Propanol and Toluene Combustion:Effect of the Preparation Method[J].Journal of Environmental Science and Health.Part A,Toxic/Hazardous Substance & Environmental Engineering,2011,46(3):291-297.
[34] CARRILLO A M,CARRIAZO J G.Cu and Co Oxides Supported on Halloysite for the Total Oxidation of Toluene[J].Applied Catalysis B:Environmental,2015,164(4):443-452.
[35] MENON U,GALVITA V V,MARIN G B.Reaction Network for the Total Oxidation of Toluene over CuO-CeO2/Al2O3[J].Journal of Catalysis,2011,283(1):1-9.
[36] TODOROVA S,NAYDENOV A,KOLEV H,et al.Mechanism of Complete n-Hexane Oxidation on Silica Supported Cobalt and Manganese Catalysts[J].Applied Catalysis A:General,2012,413(4):43-51.