乙二胺四乙酸配位螯合法制备钴铝尖晶石蓝色颜料

doi:10.3969/j.issn.1007-2985.2014.01.017

journal6 ›› 2014, Vol. 35 ›› Issue (1): 72-77.DOI: 10.3969/j.issn.1007-2985.2014.01.017

乙二胺四乙酸配位螯合法制备钴铝尖晶石蓝色颜料

胡名卫，王宏全，夏浩孚，黄志良，池汝安

（1.武汉工程大学材料科学与工程学院，湖北武汉 430074；2.武汉工程大学化工与制药学院，湖北武汉 430074）

出版日期:2014-01-25 发布日期:2014-01-25

BluePigment Cobalt-Aluminum Spinels Prepared by EDTA Chelating Method

HU Ming-Wei, WANG Hong-Quan, XIA Hao-Fu, HUANG Zhi-Liang, CHI Ru-An

(1.School of Material Science and Engineering,Wuhan Institute of Technology,Wuhan 430074,China;2.School of Chemical Engineering,Wuhan Institute of Technology,Wuhan 430074,China)

Online:2014-01-25 Published:2014-01-25
About author:HU Mingwei (1990-),male,was born in Fuzhou City,Jiangxi Province,MSLA;research area is functions and application of inorganic non-metallic materials.
Supported by:
National Natural Science Foundation of China (51374155)；National 973 Pre-Research Project (2011CB411901)

摘要/Abstract

摘要：提出一种可以在较低温度下焙烧制备出钴铝尖晶石蓝色颜料的方法.以六水合硝酸钴、九水合硝酸铝为主要原料，乙二胺四乙酸(EDTA)为配位螯合剂，通过EDTA配位螯合钴、铝得到有机配合物前驱体，经过焙烧制备钴蓝颜料.通过国际照明委员会的色度图谱(CIE)、X射线衍射(XRD)和傅里叶红外光谱(FTIR)，分别对所制备样品的物相和呈色进行研究表征.主要考察了钴铝物质的量比、反应体系pH值、焙烧温度等工艺条件对铝酸钴尖晶石相的完整性和颜料呈色的影响.制备钴铝尖晶石蓝色颜料的最佳工艺参数是900 ℃温度下保温时间为2 h，pH值为9~10，前驱体的钴铝比为 1∶2.5.

关键词： 乙二胺四乙酸, 正交试验, 尖晶石, 前驱体, 配位螯合

Abstract: A method is proposed to prepare cobalt aluminum spinel blue pigment under a relatively low temperature.Cobalt aluminum spinels were prepared by the thermal decomposition of EDTA chelating cobalt and aluminum complex precursors which are derived from metal nitrate salts and ethylenediamine tetraacetic acid (EDTA).EDTA was used for chelating agent,cobalt nitrate hexahydrate and aluminum nitrate nonahydrate were used to synthesize the precursors.The phase and coloration of the prepared samples were characterized by the Commission International Eclairage (CIE) chromaticity diagram,X-ray diffraction (XRD) and Fourier-transform infrared spectroscopy (FTIR).The main variables which can systematically investigate the coloration and crystalline phase were cobalt-aluminum ratio,pH value of the reaction system and the calcination temperature.The optimizing process parameters to prepare cobalt aluminum spinel blue pigment:the temperature is 900 ℃ with 2 h heating preservation,the pH value is 9~10,and the cobalt-aluminum mole ratio is 1∶2.5 in the precursors.

Key words: ethylenediamine tetraacetic acid, orthogonal test, spinel, precursors, chelating ligand

胡名卫, 王宏全, 夏浩孚, 黄志良, 池汝安. 乙二胺四乙酸配位螯合法制备钴铝尖晶石蓝色颜料[J]. journal6, 2014, 35(1): 72-77.

HU Ming-Wei, WANG Hong-Quan, XIA Hao-Fu, HUANG Zhi-Liang, CHI Ru-An. BluePigment Cobalt-Aluminum Spinels Prepared by EDTA Chelating Method[J]. journal6, 2014, 35(1): 72-77.

参考文献

[1] CHEMLAL S，LARBOTETC A.Materials Research Bulletin[J].Journal of the European Ceramic Society，2000，35(2)：2 515-2 523.

[2] YANG Zongzhi.Cobalt Blue Pigments and Its Progress[J].Paint & Coatings Industry，1997（4）：39-40.

[3] ZHU Jiliang,WU Shennian.Pigment Technology[M].Beijing：Chemical Industry Press，2002：293-296.

[4] ZHOU Junyi.Synthesis,Characterization and Property of Spinel Metal Oxides[D].Ji’nan:Ji’nan University,Material Science and Engineering Institute,2009.

[5] SHAO Qinghui,GU Guobang,ZHANG Lijuan,et al.Research Progress of Synthesis and Preparation of Nanophase Materials[J].Ordnance Material Science and Engineering，2005，22（4）：59-63.

[6] ALEXANDRIA,VIRGINIA.DCMA Classification and Chemical Description of the Complex Inorganic Color Pigments[J].Dry Color Manufacturers’ Association，1991，21（1）：54-58.

[7] HAN Yunfang,LI Xiangtang.Preparation of Cobalt-Blue Pigment by Sluggish Precipitation Method[J].Journal of Tianjin Institute of Urban Construction，2002，8（2）：92-95.

[8] ZHOU Yongqiang,YU Fangli,LUO Hongjie et al.Preparation of Nanometer Cobalt Blue Pigment by Sol-Gel Method[J].Bulletin of the Chinese Ceramic Society，2006，25（5）：31-33.

[9] ZHAO Ying,ZENG Yanli,ZHENG Shijun,et al.The Present Studies and Prospect on Halogen Bond[J].Journal of HeBei Normal University/Nature Science Edition，2007，31（1）：85-99.

[10] MASOUD SALAVATI-NIASARI,MASOUD FARHADI-KHOUZANI,FATEMEH DAVAR.Bright Blue Pigment CoAl2O4 Nanocrystals Prepared by Modified Sol-Gel Method[J].Sol-Gel Sci. Technol.,2009,52:321-327.

[11] CAO Liyun,DEN Fei,ZHANG Xinhe,et al.Preparation of Nano-CoAl2O4 Blue Ceramic Pigment by Microemulsion Process[J].Glass & Enamel，2005，35（5）：40-44.

[12] CHEN Jing,SHI Xiaobo，HAN Bing.The Preparation and Characteristics of Cobalt Blue Colored Mica Titania Pearlescent Pigment by Micro Emulsions[J].Dyes and Pigments,2007，75(1)：766-769.

[13] DENG Xinrong,HU Guorong,PENG Zhongdong,et al.Preparation of Superfine Sized Cobalt Blue Pigment Using Precipitation-Azeotropic Distillation Method[J].Materials Review，2006，5(20）：345-353.

[14] AI Jun,LU Xilong,WANG Weixing,et al.Synthesis of CoAl2O4 Spinel-Type Cobalt Blue Pigments via Acid Chelating Precursor Technique[J].Journal of Ceramics，2011,32（2）:178-181.

[15] CUI Yanwang,XUAN Bai,SHAO Minliu,et al.Synthesis of Cobalt-Aluminum Spinels via EDTA Chelating Precursors[J].Journal of Materials Science,2004,39:6 161-6 201.

[16] CHEN Zhizhan,SHI Erwei,ZHENG Yanqing,et al.Hydrothermal Synthesis and Optical Property of Nano-Sized CoAI2O4 Pigment[J].Materials Letters，2002，55(1)：281-289.

[17] HU Guorong,DENG Xinrong,CAOYanbing,et al.Synthesis of Spherical CoA12O4 Pigment Particles with High Reflectivity by Polymeric-Aerosol Pyrolysis[J].Science Direct，2007，26（3）：236-242.

[18] HU Guorong,CAOYanbing,DENG Xinrong,et al.Synthesis of Ultrafine Cobalt Blue Pigment Using Crystallization-Pyrolysis Process[J].Paint & Coating Industry，2006，11：15-15.

[19] CARTA G，CASARIN M，HABRA N E.MOCVD Deposition of CoAl2O4 Films[J].Electrochimica Acta，2005，50(3)：4 592-4 599.
[20] LIU Zhubo.Study of Spinel Cobalt Blue Pigment Preparation and Performance[D].Nanjing:Nanjing University of Science and Technology,Material Science and Engineering Institute,2008.

[21] ROBERT HUNTER.CIE Colorimetry[J].Jiangxi Building Materials,1996(4):31-42.

[22] YE Chunfang,LIU Wangling,YU Feihong.Realization of Active X Control of CIE Chromatic Spaces[J].Optical Instrument，2005（3）:27-32.

编辑推荐 0

Metrics

阅读次数

全文

252

HTML			PDF

最新录用	在线预览	正式出版	最新录用	在线预览	正式出版
0	0	0	0	0	252

来源	本网站	其他网站

次数	149	103
比例	59%	41%

摘要

1012

最新录用	在线预览	正式出版

0	0	1012

来源	本网站	其他网站

次数	786	226
比例	78%	22%

乙二胺四乙酸配位螯合法制备钴铝尖晶石蓝色颜料

BluePigment Cobalt-Aluminum Spinels Prepared by EDTA Chelating Method

PDF (PC)

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 7

编辑推荐 0

Metrics

本文评价

[1]	王赛群, 尹小红. 正交试验因素水平表编排的改进[J]. 吉首大学学报（自然科学版）, 2020, 41(6): 97-100.
[2]	滕春霖，张建斌，阳志军，薛连，李理，邓谦. 有机-无机杂化物：合成·表征·光致变色特性[J]. 吉首大学学报（自然科学版）, 2016, 37(3): 66-73.
[3]	刘亚倩, 魏华, 李贵, 贺建武, 陈韬, 张源, 周雰. 荠菜总黄酮质量分数测定及超声提取工艺优化[J]. journal6, 2016, 37(1): 74-79.
[4]	黄诚, 尹红. 基于超声波辅助法的杜仲籽蛋白提取工艺优化[J]. journal6, 2014, 35(1): 78-82.
[5]	金春英, 黄庆添, 林金清, 徐旭波, 李海滨. 橘皮中果胶的超声辅助溶剂法提取工艺[J]. journal6, 2007, 28(4): 111-114.
[6]	彭晓春, 周青山. 醇提-酯萃法提取竹叶中的总黄酮[J]. journal6, 2003, 24(2): 87-88.
[7]	李东升, 史振民, 秦振平, 王文亮, 王继武. 溶胶- 凝胶前体法制备纳米ZnO[J]. journal6, 2001, 22(1): 75-77.